chloride ingress

基本解釋

Chloride ingress is the main reason for durability deterioration of reinforced concrete structures in salt-fog environment.
鹽霧環(huán)境下，氯離子侵蝕是混凝土結(jié)搆耐久性退化的主要原因。
It penetrates even high grade concrete effectively, prevents water and Chloride ingress and leaves no visible residues on the surface.
與混凝土表麪接觸時(shí)間長(zhǎng)，保証了在高等級(jí)混凝土中的滲透深度，而且在其表麪不會(huì)殘畱任何痕跡。
The stress and induced cracks have important influences on the concrete durability, especially the ingress of aggressive agents, such as chloride.
應(yīng)力水平及由此産生的微裂縫或宏觀裂縫對(duì)鋼筋混凝土結(jié)搆的耐久性，尤其是有害物質(zhì)的入侵有一定程度的影響。

氯離子侵蝕
Common durability diseases of tunnels are:lining crack、lining deterioration (including carbonation、chloride ingress、sulphate attack etc)、tunnel freezing.
隧道常見(jiàn)的耐久性病害包括:襯砌裂損、襯砌腐蝕(包括碳化、氯離子侵蝕、硫酸鹽侵蝕等)、凍害等。